- Polyram RamLloy PN300G2 PPE/PS Alloy, 10% Glass Fiber
Polyram RamLloy PN300G2 PPE/PS Alloy, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy PN300G2 PPE/PS Alloy, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE/PS alloy, 10% glass fiber reinforced for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 2577 |
| Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 280 °C |
13 g/10 min @Load 22.0 lb, Temperature 536 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- RheTech Products FT1004-625UV Thermoplastic Polyolefin, UV Stabilized, Interior DX9 Black
- Polimeri Europa Extir® LN 2001 Expandable Polystyrene
- DSM Akulon® K230-HPV8 Impact Modified Nylon 6 (European Grade) (Cond) (discontinued **)
- Kennametal Stellite Deloro® 50 Nickel Alloy
- Lehmann & Voss LUVOCOM® 80-7655/RD Polyacetal-copolymer, with aramid reinforcement and PTFE, toughness-modified, high viscosity
- LG Chemical SEETEC BF415 LDPE
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
- Mearthane Durethaneâ„¢ S DS-230A Solid Polyurethane Elastomer
- Solvay Specialty Polymers Radel® R-5000 Polyphenylsulfone (PPSU)
- 3M 75 Repositionable Spray Adhesive
Copyright © lookpolymers.com All Rights Reserved