Polyram RamLloy PBB104 PC/ABS alloy, Injection Molding
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy PBB104 PC/ABS alloy, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/ABS alloy for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | DIN 53479 |
| Water Absorption | 0.60 % | 0.60 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM-D638 |
| Elongation at Break | 25 % | 25 % | ASTM-D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM-D790 |
| Izod Impact, Notched | 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Vicat Softening Point | 116 °C | 241 °F | ASTM-D1525 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
- Fiberfil® J-60/20/TT/FD WT8381 Polypropylene Homopolymer, 20% Glass Reinforced, FDA compliant
- Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes
- A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
- Zhejiang Juner 201-G0 Flame Resistant Nonreinforced
- Tra-Con Tra-Bond 716C01 Medium Viscosity Epoxy Adhesive
- Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced
- DuPont Performance Polymers Delrin® 127UV NC010 Acetal (POM) (Unverified Data**)
- Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Conditioned)
Copyright © lookpolymers.com All Rights Reserved