Polyram PlusTek RA702 Nylon 66 for Injection Molding, UV Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Polyram
Trade Name PlusTek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram PlusTek RA702 Nylon 66 for Injection Molding, UV Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
UV stabilized Nylon 66 for injection molding applications.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.8 %
2.8 %
50% RH; ISO 62
Water Absorption at Saturation 8.5 %
8.5 %
ISO 62
Linear Mold Shrinkage 0.011 - 0.018 cm/cm
0.011 - 0.018 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527
Elongation at Break 35 %
35 %
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
Izod Impact, Notched (ISO) 4.40 kJ/m²
2.09 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 11357
Maximum Service Temperature, Air 110 °C
230 °F
Continuous use
180 °C
356 °F
Short peaks operation
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75
Flammability, UL94 V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 120 kV/mm
3050 kV/in
IEC 60250