Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 95.1 MPa @Thickness 3.17 mm |
13800 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.17 mm |
3.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 160 MPa @Thickness 3.17 mm |
23200 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 6.60 GPa @Thickness 3.17 mm |
957 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 0.399 J/cm @Thickness 3.17 mm |
0.748 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |