Polyram PlusTek RA325G4 Nylon 66 for Injection Molding, 20% Glass-Fiber Reinforced, Self-Extinguishing, Halogen Free
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA325G4 Nylon 66 for Injection Molding, 20% Glass-Fiber Reinforced, Self-Extinguishing, Halogen Free.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass-fiber reinforced, self-extinguishing halogen free Nylon 66 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.5 % | 6.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0045 - 0.0055 cm/cm | 0.0045 - 0.0055 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous use |
| 240 °C | 464 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N60N Nitrile Rubber
- SABIC Innovative Plastics Lexan® IR2520 PC
- LG Chemical LUMID GP2251BF PA66+GF25%, Flame Retardant
- IRPC Polimaxx Polene GG3245 High Density Polyethylene
- Samyang Tribit® 1700 PBT, Middle Viscosity
- Dow Corning SE 738 SILICONE RTV
- Chosun Refractories LWB-135 Casting Block
- Eurostar Star C BX6088 ABS, 20% Carbon Filled, Injection Molding
- ExxonMobil Label-Lyte™ 150LL-302 OPP Film
Copyright © lookpolymers.com All Rights Reserved