Polyram PlusTek RA314G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Polyram
Trade Name PlusTek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram PlusTek RA314G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass fiber reinforced, heat stabilized Nylon 66 for injection molding applications.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.6 %
1.6 %
50% RH; ISO 62
Water Absorption at Saturation 4.0 %
4.0 %
ISO 62
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ISO 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
Tensile Strength, Yield 210 MPa
30500 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
Flexural Strength 290 MPa
42100 psi
ISO 178
Flexural Modulus 9.80 GPa
1420 ksi
ISO 178
Izod Impact, Notched (ISO) 13.5 kJ/m²
6.42 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 11357
Maximum Service Temperature, Air 120 °C
248 °F
Continuous use
230 °C
446 °F
Short peaks operation
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60250