Polyram PlusTek PA341G9 Nylon 6.6, 45% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA341G9 Nylon 6.6, 45% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
45% glass fiber reinforced, high stiffness and extreme cold environment, UV stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | DIN 53479 |
| Water Absorption | 3.5 % | 3.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM-D785 |
| Tensile Strength, Yield | 165 MPa | 23900 psi | ASTM-D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM-D638 |
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.90 J/cm @Temperature 23.0 °C |
3.56 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| >= 200 °C | >= 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Indium Corp. 6N High Purity Indium Metal
- Shin-Etsu Silicones KSG-43 Fluid
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Over-Cured
- CTC X-PRO TF 1113 HP Polypropylene Homopolymer, 13% Talc Filled
- ConocoPhillips Hydroclear® 22 Quench Oil
- Eurotec® Tecotek® PC30 GR20 GR003 ZG20 PC, 20% glass fiber reinforced, flame retardant - halogen (RoHS compliant), grey RAL 7035
- Arlon R31031R025 0.025" Uncured Silicone Rubber with Fiberglass Substrate
- 3M FP024902 White Polypropylene Label Products
- Bulk Molding Compounds BMC 851 Corrosion Resistant, Flame Retardant Molding Compound
Copyright © lookpolymers.com All Rights Reserved