Polyram PlusTek PA340S6 Nylon 6.6, 30% Glass beads
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA340S6 Nylon 6.6, 30% Glass beads.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass beads reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | DIN 53479 |
| Water Absorption | 5.6 % | 5.6 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM-D785 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM-D790 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- NatureWorks® Ingeo™ 3251D Injection Grade PLA
- Premix Thermoplastics PRE-ELEC® TPE 1502 Conductive Thermoplastic Compound
- ExxonMobil Santoprene® 121-60W228 Thermoplastic Elastomer (discontinued **)
- LyondellBasell Pro-fax SB787 Polypropylene Impact Copolymer
- LG Chemical LUTENE LB7500 LDPE Extrusion Coating
- LyondellBasell Adsylâ„¢ 3 C 37 F HP Polypropylene Copolymer
- SABIC Innovative Plastics Noryl PC180X PPE+PS
- Formosa Plastics Formolene® HP3902 Pipe HDPE
Copyright © lookpolymers.com All Rights Reserved