Polyram PA310G8 Nylon 66, 40% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PA310G8 Nylon 66, 40% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | DIN 53479 |
| Water Absorption | 4.7 % | 4.7 % | DIN 53495 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 210.0 MPa @Thickness 3.17 mm |
30460 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 2.0 % @Thickness 3.17 mm |
2.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 320 MPa @Thickness 3.17 mm |
46400 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 13.5 GPa @Thickness 3.17 mm |
1960 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm @Thickness 3.17 mm |
2.43 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |