Polyplastic Armlen® PP-2FR Polypropylene, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Polyplastic Group |
| Trade Name | Armlen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyplastic Armlen® PP-2FR Polypropylene, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, RoHS compliantInformation provided by PolyPlastic Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
| Elongation at Break | 43 % | 43 % | ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
IEC 60695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 °C | 428 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Drying Temperature | 80.0 °C @Time 7200 sec |
176 °F @Time 2.00 hour |
Users viewing this material also viewed the following:
- Potters Industries Ballotini® Impact Beads
- Hong Kun Group UV 327 UV Absorber
- Ineos N20L-00 Polypropylene Impact Copolymer
- Eagle Brass 302 Austenitic Stainless Steel, 1/4 Hardened
- Esstech V-116-1130 Barium Silicate Glass
- DuPont Teijin Films Melinex® 194 Polyester Film, 380 Gauge
- Asahi Kasei Thermofil P-20TC-5100 20% Talc Filled, Heat Stabilized
- Arlon R35232B085 0.085" (2.16 mm) Fully Cured Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved