Polyplastic Armamid® PA6 GF 30-2HSM-902 Nylon, 30% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Polyplastic Group
Trade Name Armamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyplastic Armamid® PA6 GF 30-2HSM-902 Nylon, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Heat stabilizedInformation provided by PolyPlastic Group.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 9.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
ISO 527-1/-2
Elongation at Break 4.9 %
4.9 %
ISO 527-1/-2
Tensile Modulus 9.20 GPa
1330 ksi
ISO 527-1/-2
Flexural Strength 240 MPa
34800 psi
ISO 178
Flexural Modulus 7.90 GPa
1150 ksi
ISO 178
Charpy Impact Unnotched 6.30 J/cm²

@Temperature -30.0 °C
 30.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
399 °F
ISO 75-1/-2
Processing Properties Metric English Comments
Melt Temperature 260 - 270 °C
500 - 518 °F
Mold Temperature 80.0 °C
176 °F
Drying Temperature 85.0 °C

@Time 7200 - 14400 sec
 185 °F

@Time 2.00 - 4.00 hour