Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate, Structural Foam, 10% Glass ReinforcedProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 8.0 - 18 g/10 min

@Load 2.16 kg,
Temperature 250 °C
8.0 - 18 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Tensile Strength, Yield 72.4 MPa
10500 psi
ASTM D638
Flexural Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 2.96 GPa
430 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
1.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 32.4 µm/m-°C

@Temperature -20.0 - 150 °C
18.0 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Vicat Softening Point 221 °C
430 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746
105 °C

@Thickness 3.00 mm
221 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746
105 °C

@Thickness 3.00 mm
221 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746
105 °C

@Thickness 3.00 mm
221 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.5

@Frequency 1000 Hz
3.5

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 27.2 kV/mm
690 kV/in
ASTM D149
Dissipation Factor 0.0014

@Frequency 1000 Hz
0.0014

@Frequency 1000 Hz
ASTM D150
0.0046

@Frequency 1.00e+9 Hz
0.0046

@Frequency 1.00e+9 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 249 - 260 °C
480 - 500 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 82.2 - 121 °C
180 - 250 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour