- Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage
Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ASTM D955 |
| Melt Flow | 10 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 3.28 GPa | 475 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C |
1.40 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 254 °C | 470 - 490 °F | |
| Middle Barrel Temperature | 249 - 260 °C | 480 - 500 °F | |
| Front Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Melt Temperature | 254 - 277 °C | 490 - 530 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.001 |
Users viewing this material also viewed the following:
- MV Labs CO800 Co3O4 Cobalt(II,III) oxide
- Isoflon PEEK Polyetheretherketone
- Momentive Performance Materials Silplusâ„¢ 30 HS High Strength Heat Cured Rubber
- Styrolution PS 2710 HIPS
- Techmer ES Elastoblend® PA6/ABS 1120 B1
- Aleris HOGAL 5558 Aluminum 5026-O/H111
- Multibase Multibatch® MP 53735 Injection Molding
- BASF Capron® 8234G 44% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- DuPont Performance Polymers Hytrel® G3548 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved