Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate, 30% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.62 g/cc
1.62 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 9.0 - 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 9.0 - 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
ASTM D638
Tensile Strength, Yield 114 MPa
16500 psi
ASTM D638
Flexural Strength 176 MPa
25500 psi
ASTM D790
Flexural Modulus 7.24 GPa
1050 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Temperature 22.8 °C
 1.20 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
ASTM D648
UL RTI, Electrical 140 °C

@Thickness 0.851 mm
 284 °F

@Thickness 0.0335 in
 UL 746
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
 UL 746
140 °C

@Thickness 2.30 mm
 284 °F

@Thickness 0.0906 in
 UL 746
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 140 °C

@Thickness 0.851 mm
 284 °F

@Thickness 0.0335 in
 UL 746
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
 UL 746
140 °C

@Thickness 2.30 mm
 284 °F

@Thickness 0.0906 in
 UL 746
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 130 °C

@Thickness 0.851 mm
 266 °F

@Thickness 0.0335 in
 UL 746
130 °C

@Thickness 1.60 mm
 266 °F

@Thickness 0.0630 in
 UL 746
130 °C

@Thickness 2.30 mm
 266 °F

@Thickness 0.0906 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 0.850 mm
 V-0

@Thickness 0.0335 in
V-0 - 5VA

@Thickness 2.30 mm
 V-0 - 5VA

@Thickness 0.0906 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 22.8 kV/mm
580 kV/in
ASTM D149
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 0.851 mm
 15 - 30 sec

@Thickness 0.0335 in
 UL 746
30 - 60 sec

@Thickness 1.60 mm
 30 - 60 sec

@Thickness 0.0630 in
 UL 746
30 - 60 sec

@Thickness 2.30 mm
 30 - 60 sec

@Thickness 0.0906 in
 UL 746
60 - 120 sec

@Thickness 3.00 mm
 60 - 120 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.851 mm
 >= 120 arcs

@Thickness 0.0335 in
 UL 746
>= 120 arcs

@Thickness 1.60 mm
 >= 120 arcs

@Thickness 0.0630 in
 UL 746
>= 120 arcs

@Thickness 2.30 mm
 >= 120 arcs

@Thickness 0.0906 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 71.1 - 87.8 °C
160 - 190 °F
Drying Temperature 116 - 121 °C
240 - 250 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005