Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction relative to unfoamed parts.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Melt Flow 25 - 45 g/10 min
25 - 45 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 29.0 MPa
4200 psi
ASTM D638
Tensile Strength, Yield 27.6 MPa
4000 psi
ASTM D638
Flexural Strength 50.3 MPa
7300 psi
ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
ASTM D790
Izod Impact, Unnotched 2.14 J/cm
4.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 82.2 °C
180 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
ASTM D648
Flammability, UL94 V-0
V-0
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 260 °C
450 - 500 °F
Middle Barrel Temperature 271 - 304 °C
520 - 580 °F
Front Barrel Temperature 271 - 304 °C
520 - 580 °F
Melt Temperature 271 - 304 °C
520 - 580 °F
Mold Temperature 65.6 - 82.2 °C
150 - 180 °F
Drying Temperature 71.1 - 82.2 °C
160 - 180 °F
Dry Time 3 - 4 hour
3 - 4 hour