Polymer Resources PPX-SF2 Modified-PPO, Structural Foam Grade, Flame Retardant

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-SF2 Modified-PPO, Structural Foam Grade, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, Structural Foam Grade, Standard FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Melt Flow 25 - 45 g/10 min

@Load 11.6 kg,
Temperature 250 °C
 25 - 45 g/10 min

@Load 25.6 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.7 MPa
7500 psi
ASTM D638
Tensile Strength, Yield 52.4 MPa
7600 psi
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Temperature 22.8 °C
 3.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 °C
220 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.9 °C
210 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
65.0 °C

@Thickness 5.99 mm
 149 °F

@Thickness 0.236 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
65.0 °C

@Thickness 5.99 mm
 149 °F

@Thickness 0.236 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
65.0 °C

@Thickness 5.99 mm
 149 °F

@Thickness 0.236 in
 UL 746
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 6.00 mm
 V-0

@Thickness 0.236 in
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 260 °C
450 - 500 °F
Middle Barrel Temperature 271 - 304 °C
520 - 580 °F
Front Barrel Temperature 271 - 304 °C
520 - 580 °F
Melt Temperature 271 - 304 °C
520 - 580 °F
Mold Temperature 65.6 - 82.2 °C
150 - 180 °F
Drying Temperature 71.1 - 82.2 °C
160 - 180 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour