Polymer Resources PPX-GP3-IM Modified-PPO, Impact Modified

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-GP3-IM Modified-PPO, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, Impact Modified, 235F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 12 - 18 g/10 min

@Load 11.6 kg,
Temperature 250 °C
12 - 18 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.4 MPa
6300 psi
ASTM D638
Tensile Strength, Yield 46.9 MPa
6800 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ASTM D638
Flexural Strength 72.4 MPa
10500 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
Izod Impact, Notched 2.14 J/cm

@Temperature -30.0 °C
4.00 ft-lb/in

@Temperature -22.0 °F
ASTM D256
4.27 J/cm

@Temperature 22.8 °C
8.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Izod Impact, Notched (ISO) 14.7 kJ/m²

@Temperature -30.0 °C
7.00 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
31.5 kJ/m²

@Temperature 22.8 °C
15.0 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 3.15 J/cm²

@Temperature 22.8 °C
15.0 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
ASTM D648
Vicat Softening Point 127 °C
260 °F
120°C/h, 50 N; ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 243 - 293 °C
470 - 560 °F
Middle Barrel Temperature 254 - 299 °C
490 - 570 °F
Front Barrel Temperature 266 - 304 °C
510 - 580 °F
Melt Temperature 274 - 302 °C
525 - 575 °F
Mold Temperature 65.6 - 98.9 °C
150 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0015