Polymer Resources PPX-G30 Modified-PPO, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-G30 Modified-PPO, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ASTM D955
Melt Flow 1.0 - 8.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
1.0 - 8.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 108
108
ASTM D785
Tensile Strength at Break 103 MPa
15000 psi
ASTM D638
Tensile Strength, Yield 103 MPa
15000 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Strength 131 MPa
19000 psi
ASTM D790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature -30.0 °C
1.00 ft-lb/in

@Temperature -22.0 °F
ASTM D256
0.801 J/cm

@Temperature 22.8 °C
1.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Charpy Impact, Notched 0.630 J/cm²

@Temperature 22.8 °C
3.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 143 °C
290 °F
ASTM D648
Vicat Softening Point 152 °C
305 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 304 °C
500 - 580 °F
Middle Barrel Temperature 271 - 310 °C
520 - 590 °F
Front Barrel Temperature 282 - 316 °C
540 - 600 °F
Melt Temperature 293 - 316 °C
560 - 600 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0015