Polymer Resources PC/TP-GP1-HF PC/Polyester Alloy, High Melt Flow
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC/TP-GP1-HF PC/Polyester Alloy, High Melt Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Melt Flow, Good Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 15 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 - 20 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |
| Front Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Melt Temperature | 246 - 274 °C | 475 - 525 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Enviramid™ N1340MGHL BK Post Consumer Recycle Nylon 66, 25/15% Mineral/Glass Filled
- SABIC Innovative Plastics NORYL PKN4775 PPE+PS (Asia Pacific)
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- Trelleborg Emerson & Cuming Eccobond® D 275 One-Component Fast Cure Epoxy Adhesive
- Zylog Hipolyene® 8025 HC Thermoplastic Polyolefin & PP Compound
- Chevron Phillips K-Resin® BK10 Styrene-Butadiene Copolymer, Injection Molding Grade
- DSM Arnitel® EL740 Polyether Ester Elastomer (European and Asian Grade)
- DuPont Performance Polymers Crastin® FGS600F40 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Diamond Polymers NPP10-0105 Vinyl Acetate Copolymer
- Eurostar Staramide BG3H PA6, 15% Glass Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved