Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Resources PC/ABS-GP1-[color]-3 PC Blend, General Purpose, UV-stabilized

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Thermoplastic Polyurethane Blend , Polyurethane, TP
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/ABS-GP1-[color]-3 PC Blend, General Purpose, UV-stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 14 - 15 g/10 min
14 - 15 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.8 MPa
7800 psi
ASTM D638
Tensile Strength, Yield 52.4 MPa
7600 psi
ASTM D638
Flexural Strength 72.4 MPa
10500 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
Izod Impact, Notched 4.81 J/cm
9.00 ft-lb/in
ASTM D256
Gardner Impact >= 36.2 J
>= 26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.9 °C
210 °F
ASTM D648
Flammability, UL94 HB
HB
1/8 in
HB
HB
1/16 in
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 288 °C
480 - 550 °F
Middle Barrel Temperature 254 - 293 °C
490 - 560 °F
Front Barrel Temperature 260 - 302 °C
500 - 575 °F
Melt Temperature 274 - 302 °C
525 - 575 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 76.7 - 82.2 °C
170 - 180 °F
Dry Time 3 - 4 hour
3 - 4 hour