Polymer Resources PC-G20 Polycarbonate, 20% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-G20 Polycarbonate, 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate, 20% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ASTM D955
Melt Flow 4.0 - 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
4.0 - 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
Tensile Strength, Yield 117 MPa
17000 psi
ASTM D638
Flexural Strength 124 MPa
18000 psi
ASTM D790
Flexural Modulus 5.17 GPa
750 ksi
ASTM D790
Izod Impact, Notched 0.801 J/cm

@Temperature 22.8 °C
1.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
285 °F
ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness 1.70 mm
176 °F

@Thickness 0.0669 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.70 mm
176 °F

@Thickness 0.0669 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.70 mm
176 °F

@Thickness 0.0669 in
UL 746
80.0 °C

@Thickness 3.00 mm
176 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-2

@Thickness 1.70 mm
V-2

@Thickness 0.0669 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 293 - 316 °C
560 - 600 °F
Middle Barrel Temperature 304 - 327 °C
580 - 620 °F
Front Barrel Temperature 316 - 338 °C
600 - 640 °F
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour