Polymer Resources NY66-IM2-[color]-H Impact Modified Nylon 66, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-IM2-[color]-H Impact Modified Nylon 66, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 66, Superior Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Linear Mold Shrinkage 0.017 - 0.020 cm/cm
0.017 - 0.020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Tensile Strength, Yield 51.7 MPa
7500 psi
ASTM D638
Flexural Strength 62.1 MPa
9000 psi
ASTM D790
Flexural Modulus 1.69 GPa
245 ksi
ASTM D790
Izod Impact, Notched 8.54 J/cm

@Temperature 22.8 °C
16.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 213 °C
415 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 68.3 °C
155 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 266 - 277 °C
510 - 530 °F
Middle Barrel Temperature 271 - 282 °C
520 - 540 °F
Front Barrel Temperature 277 - 288 °C
530 - 550 °F
Melt Temperature 277 - 293 °C
530 - 560 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0003