Polymer Resources NY66-IM1-G33 Nylon 66, 33% Glass Reinforced, Toughened

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-IM1-G33 Nylon 66, 33% Glass Reinforced, Toughened.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 66, 33% Glass Reinforced, Toughened and LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0080 cm/cm
0.0030 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 128 MPa
18500 psi
ASTM D638
Tensile Strength, Yield 128 MPa
18500 psi
ASTM D638
Flexural Strength 200 MPa
29000 psi
ASTM D790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm

@Temperature 22.8 °C
2.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 243 °C
470 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 271 - 282 °C
520 - 540 °F
Middle Barrel Temperature 282 - 299 °C
540 - 570 °F
Front Barrel Temperature 282 - 304 °C
540 - 580 °F
Melt Temperature 288 - 304 °C
550 - 580 °F
Mold Temperature 82.2 - 104 °C
180 - 220 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005