Polymer Resources NY66-GP2 General Purpose Nylon 66, Nucleated

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources NY66-GP2 General Purpose Nylon 66, Nucleated.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

General Purpose Nylon 66, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Linear Mold Shrinkage	0.012 - 0.018 cm/cm	0.012 - 0.018 in/in	Flow; ASTM D955
	0.015 - 0.021 cm/cm	0.015 - 0.021 in/in	Across Flow; ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	89.6 MPa	13000 psi	ASTM D638
Tensile Strength, Yield	89.6 MPa	13000 psi	ASTM D638
Elongation at Break	30 %	30 %	ASTM D638
Elongation at Yield	4.5 %	4.5 %	ASTM D638
Tensile Modulus	3.38 GPa	490 ksi	ASTM D638
Flexural Strength	117 MPa	17000 psi	ASTM D790
Flexural Modulus	3.03 GPa	440 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Temperature 22.8 °C	1.00 ft-lb/in @Temperature 73.0 °F	ASTM D256
Izod Impact, Notched (ISO)	3.15 kJ/m² @Temperature 22.8 °C	1.50 ft-lb/in² @Temperature 73.0 °F	ISO 180/1A
Charpy Impact, Notched	0.378 J/cm² @Temperature -30.0 °C	1.80 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.420 J/cm² @Temperature 22.8 °C	2.00 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	246 °C	475 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	102 °C	215 °F	ASTM D648
Flammability, UL94	V-2 @Thickness 1.59 mm	V-2 @Thickness 0.0626 in
	V-2 @Thickness 3.17 mm	V-2 @Thickness 0.125 in

Processing Properties	Metric	English
Rear Barrel Temperature	266 - 277 °C	510 - 530 °F
Middle Barrel Temperature	271 - 282 °C	520 - 540 °F
Front Barrel Temperature	277 - 288 °C	530 - 550 °F
Melt Temperature	277 - 293 °C	530 - 560 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	73.9 - 85.0 °C	165 - 185 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.0003