Polymer Resources NY66-GP1 General Purpose Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-GP1 General Purpose Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General Purpose Nylon 66, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Linear Mold Shrinkage 0.012 - 0.018 cm/cm
0.012 - 0.018 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.7 MPa
12000 psi
ASTM D638
Tensile Strength, Yield 82.7 MPa
12000 psi
ASTM D638
Flexural Strength 117 MPa
17000 psi
ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
 1.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 229 °C
445 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 266 - 277 °C
510 - 530 °F
Middle Barrel Temperature 271 - 282 °C
520 - 540 °F
Front Barrel Temperature 277 - 288 °C
530 - 550 °F
Melt Temperature 277 - 293 °C
530 - 560 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0003