Polykemi AB SCANMID 6 B52^ E Nylon 6, Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B52^ E Nylon 6, Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
With Flow; ISO 2577
0.016 cm/cm
0.016 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 70

@Time 15.0 sec
70

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break <= 55.0 MPa
<= 7980 psi
ISO/R527
Elongation at Break >= 100 %
>= 100 %
ISO/R527
Elongation at Yield 4.0 %
4.0 %
ISO/R527
Flexural Strength <= 80.0 MPa
<= 11600 psi
ISO 178
Flexural Modulus 2.00 GPa

@Temperature 23.0 °C
290 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 2.50 J/cm²

@Temperature -20.0 °C
11.9 ft-lb/in²

@Temperature -4.00 °F
ISO 179
5.50 J/cm²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
120°C/h; ISO 75/1
Vicat Softening Point 160 °C

@Load 5.001 kg
320 °F

@Load 11.03 lb
50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 695-2-1