Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer Polykemi AB
Trade Name SCANBLEND
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
With Flow; ISO 2577
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Across Flow; ISO 2577
Melt Index of Compound 40 g/10 min

@Load 5.00 kg,
Temperature 260 °C
40 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 48.0 MPa
<= 6960 psi
ISO/R527
Elongation at Yield 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 83.0 MPa
<= 12000 psi
ISO 178
Flexural Modulus 2.40 GPa

@Temperature 23.0 °C
348 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
120°C/h; ISO 75/1
Vicat Softening Point 122 °C

@Load 5.001 kg
252 °F

@Load 11.03 lb
50°C/h; ISO 306
138 °C

@Load 1.00 kg
280 °F

@Load 2.21 lb
50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 695-2-1