Polykemi AB POLYshine PBT D204 GF30 FR PBT, Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Polykemi AB
Trade Name POLYshine
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYshine PBT D204 GF30 FR PBT, Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.012 cm/cm
0.012 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 145 MPa
<= 21000 psi
ISO/R527
Elongation at Break 1.8 %
1.8 %
ISO/R527
Flexural Strength <= 185 MPa
<= 26800 psi
ISO 178
Flexural Modulus 9.00 GPa

@Temperature 23.0 °C
1310 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
ISO 179
0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
120°C/h; ISO 75/1
Vicat Softening Point 210 °C

@Load 5.001 kg
410 °F

@Load 11.03 lb
50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.00 mm
V-0

@Thickness 0.0394 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 695-2-1