Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Filler Content 20 %
20 %
±2%; Polykemi
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
With Flow; ISO 2577
0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
Across Flow; ISO 2577
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 230 °C
15 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 28.0 MPa
<= 4060 psi
ISO/R527
Elongation at Yield 8.0 %
8.0 %
ISO/R527
Flexural Strength <= 44.0 MPa
<= 6380 psi
ISO 178
Flexural Modulus 1.80 GPa

@Temperature 23.0 °C
261 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.250 J/cm²

@Temperature -20.0 °C
1.19 ft-lb/in²

@Temperature -4.00 °F
ISO 179
0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
120°C/h; ISO 75/1
Vicat Softening Point 81.0 °C

@Load 5.001 kg
178 °F

@Load 11.03 lb
50°C/h; ISO 306
142 °C

@Load 1.00 kg
288 °F

@Load 2.21 lb
50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
1380 °F

@Thickness 0.0787 in
IEC 695-2-1