Polykemi AB POLYfill PPH T15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPH T15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ISO 1183
Filler Content 10 %
10 %
±2%; Polykemi
Linear Mold Shrinkage 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
With Flow; ISO 2577
0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
Across Flow; ISO 2577
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 31.0 MPa
<= 4500 psi
ISO/R527
Elongation at Yield 12 %
12 %
ISO/R527
Flexural Strength <= 45.0 MPa
<= 6530 psi
ISO 178
Flexural Modulus 1.80 GPa

@Temperature 23.0 °C
 261 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 101 °C
214 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
120°C/h; ISO 75/1
Vicat Softening Point 67.0 °C

@Load 5.001 kg
 153 °F

@Load 11.03 lb
 50°C/h; ISO 306
134 °C

@Load 1.00 kg
 273 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in