Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
| Elongation at Break | 55 % | 55 % | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 37.0 MPa | <= 5370 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 - 80.0 µm/m-°C | 33.3 - 44.4 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 63.0 °C @Load 5.001 kg |
145 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 139 °C @Load 1.00 kg |
282 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Scratch Resistance, 10N (dL) | 0.12 | 10N Fine Structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Niche Polymer PA66BK Nylon 66
- Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized
- DSM Akulon® S223-E Nylon 66 (European and Asian Grade) (Cond) (discontinued **)
- Lanxess Pocan® KU 2-7604 000000 PBT+PC
- SABIC Innovative Plastics ULTEM HU1110 PEI (Asia Pacific)
- Shin-Etsu Silicones SV-58000U High Strength Silicone Elastomer
- Techmer ES Luriblend® PA6/6 M/TL7 HS L Nylon 66
- DSM Akulon® F136-DH Nylon 6 (European Grade) (Dry)
- DSM Akulon® K222-KGMV14 Nylon 6-25% Glass and Mineral Reinforced (European Grade) (Cond)
- Master Bond Supreme 3AN One Component, Heat Curing Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved