- Polykemi AB POLYelast TPE Z700 Thermoplastic Elastomer, SEBS-based
Polykemi AB POLYelast TPE Z700 Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z700 Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | With Flow; ISO 2577 |
| 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 @Time 15.0 sec |
70 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 10.0 MPa | <= 1450 psi | ISO/R527 |
| Elongation at Break | 675 % | 675 % | ISO/R527 |
| 100% Modulus | 0.00290 GPa | 0.421 ksi | ISO/R527 |
| 300% Modulus | 0.00400 GPa | 0.580 ksi | ISO/R527 |
| Tear Strength | 28.0 kN/m | 160 pli | D624 |
| Compression Set | 28 % @Temperature 23.0 °C, Time 259000 sec |
28 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 43 % @Temperature 70.0 °C, Time 86400 sec |
43 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- RheTech Products G13P100-347UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, 109D Medium Pewter
- Precision Polymer Engineering N90M Nitrile Rubber
- SABIC Innovative Plastics Lexan® 923A PC (Europe-Africa-Middle East)
- Chevron Phillips mPact™ D353 m-MDPE Linear Low Density Polyethylene (discontinued **)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 1.0 PHR MBT
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Suprex Clay Filler
- Eastman Tenite 360A4861307 Cellulose Acetate Propionate, Clear, Trsp
- Eastman Tenite 371A4000012 Cellulose Acetate Propionate, Clear, Trsp
Copyright © lookpolymers.com All Rights Reserved