Polykemi AB POLYasa 2008F UV-stabilized, High Flow ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Polykemi AB
Trade Name POLYasa
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYasa 2008F UV-stabilized, High Flow ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
With Flow; ISO 2577
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Across Flow; ISO 2577
Melt Index of Compound 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 50.0 MPa
<= 7250 psi
ISO/R527
Elongation at Yield 5.5 %
5.5 %
ISO/R527
Flexural Strength <= 86.0 MPa
<= 12500 psi
ISO 178
Flexural Modulus 2.50 GPa

@Temperature 23.0 °C
363 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
120°C/h; ISO 75/1
Vicat Softening Point 95.0 °C

@Load 5.001 kg
203 °F

@Load 11.03 lb
50°C/h; ISO 306
103 °C

@Load 1.00 kg
217 °F

@Load 2.21 lb
50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in fresh-air dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi
Back Pressure 1.00 - 1.50 MPa
145 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High