Polycasa Acryl® G 88 Acrylic

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded
Manufacturer Polycasa
Trade Name Acryl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polycasa Acryl® G 88 Acrylic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glazing, domed roof lights, lighting covers, publicity lighting, reflectors, lenses, instrument covers, dishes and bowls; mostly used in the automotive industry.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Moisture Absorption at Equilibrium 0.30 %
0.30 %
Linear Mold Shrinkage, Flow 0.0065 cm/cm
0.0065 in/in
Melt Flow 2.1 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.1 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 75.0 MPa
10900 psi
Elongation at Break 3.5 %
3.5 %
Tensile Modulus 3.30 GPa
479 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Tensile Creep Modulus, 1000 hours 1400 MPa
203000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 103 °C
217 °F
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Vicat Softening Point 108 °C
226 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Oxygen Index 18 %
18 %
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
Dielectric Strength 60.0 kV/mm
1520 kV/in
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
0.040

@Frequency 100 Hz
0.040

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V