PolyOne Versaflex™ OM 9-801N Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versaflex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versaflex™ OM 9-801N Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versaflex™ OM 9-801N is designed for overmolding onto a wide variety of substrates including PC, ABS, PC/ABS, HIPS, PPO, acetal, acrylic and copolyester. - Bonds to a Variety Of Substrates - Rubbery Feel - Soft Touch - Very Good Surface AestheticsColor concentrates with polyethylene (PE) or EVA carriers are most suitable for coloring Versaflex™ OM 9-801N. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polystyrene (PS) or polypropylene (PP). Regrind levels up to 20% can be used with Versaflex™ OM 9-801N with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versaflex™ OM 9-801N has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 5 - 8 minutes or longer. Drying is not Required Injection Speed: 0.5 to 3 in/sec 1st Stage - Boost Pressure: 500 to 900 psi 2nd Stage - Hold Pressure: 70% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Viscosity 15600 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
15600 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Linear Mold Shrinkage, Flow 0.0030 - 0.0090 cm/cm
0.0030 - 0.0090 in/in
ASTM D955
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 190 °C
22 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
100 g/10 min

@Load 5.00 kg,
Temperature 200 °C
100 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 47
47
10 sec; ASTM D2240
Tensile Strength at Break 4.49 MPa

@Temperature 23.0 °C
651 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.45 MPa

@Strain 100 %,
Temperature 23.0 °C
210 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
1.80 MPa

@Strain 300 %,
Temperature 23.0 °C
261 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 820 %

@Temperature 23.0 °C
820 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 17.5 kN/m
99.9 pli
ASTM D624
Compression Set 43 %

@Temperature 23.0 °C,
Time 79200 sec
43 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 182 - 193 °C
360 - 379 °F
Middle Barrel Temperature 188 - 202 °C
370 - 396 °F
Front Barrel Temperature 193 - 204 °C
379 - 399 °F
Nozzle Temperature 199 - 218 °C
390 - 424 °F
Mold Temperature 21.1 - 37.8 °C
70.0 - 100 °F
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi
Screw Speed 75 - 125 rpm
75 - 125 rpm
Descriptive Properties Value Comments
Agency Ratings FDA Unspecified Rating
UL 94 .QMFZ2.E76261
Appearance Natural Color
Automotive Specifications FMVSS 302
Features Good Surface Finish
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Flexible Grips
General Purpose
Overmolding
Soft Touch Applications
Sporting Goods