- PolyOne Versaflex™ HC 2110-43N Thermoplastic Elastomer (TPE)
PolyOne Versaflex™ HC 2110-43N Thermoplastic Elastomer (TPE)
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | PolyOne Corporation |
| Trade Name | Versaflex™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Versaflex™ HC 2110-43N Thermoplastic Elastomer (TPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Versaflex™ HC 2110-43N is a unique TPE designed for the demanding requirements of gaskets and stoppers used in healthcare and food packaging applications. New Product. Commercial specifications have not been established. - Good Compression Set - Good Reseal CharacteristicsPurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Versaflex™ HC 2110-43N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 3 in/sec 1st Stage - Boost Pressure: 25 to 1000 psi 2nd Stage - Hold Pressure: 30% of Boost Hold Time (Thick Part): 3 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.978 g/cc | 0.978 g/cc | ASTM D792 |
| Viscosity | 10500 cP @Shear Rate 11200 1/s, Temperature 200 °C |
10500 cP @Shear Rate 11200 1/s, Temperature 392 °F |
ASTM D3835 |
| 52700 cP @Shear Rate 1340 1/s, Temperature 200 °C |
52700 cP @Shear Rate 1340 1/s, Temperature 392 °F |
ASTM D3835 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 43 | 43 | 10 sec; ASTM D2240 |
| Tensile Strength at Break | 4.98 MPa @Temperature 23.0 °C |
722 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
| Tensile Stress | 0.924 MPa @Strain 100 %, Temperature 23.0 °C |
134 psi @Strain 100 %, Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
| 2.54 MPa @Strain 300 %, Temperature 23.0 °C |
368 psi @Strain 300 %, Temperature 73.4 °F |
Die C2 hr; ASTM D412 | |
| Elongation at Break | 710 % @Temperature 23.0 °C |
710 % @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
| Compression Set | 12 % @Temperature 23.0 °C, Time 79200 sec |
12 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395B |
| 22 % @Temperature 70.0 °C, Time 79200 sec |
22 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 193 °C | 340 - 379 °F | |
| Middle Barrel Temperature | 193 - 243 °C | 379 - 469 °F | |
| Front Barrel Temperature | 204 - 254 °C | 399 - 489 °F | |
| Nozzle Temperature | 216 - 254 °C | 421 - 489 °F | |
| Mold Temperature | 15.6 - 37.8 °C | 60.1 - 100 °F | |
| Back Pressure | 0.000 - 0.827 MPa | 0.000 - 120 psi | |
| Screw Speed | 25 - 100 rpm | 25 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ISO 10993 Part 4 | |
| ISO 10993 Part 5 | ||
| USP Class VI | ||
| Appearance | Natural Color | |
| Generic Material | TPE | |
| Generic Name | Thermoplastic Elastomer (TPE) | |
| Manufacturer / Supplier | GLS Thermoplastic Elastomers | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |