PolyOne Trilliant™ HC HC6620-0033 RS Natural Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Trilliant™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Trilliant™ HC HC6620-0033 RS Natural Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead of the competition. When specified, Trilliant® compounds may incorporate agency rated materials that meet USP Class VI, FDA or ISO 10993 testing requirements.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 190 MPa | 27600 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 282 - 293 °C | 540 - 559 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 245 °C @Thickness 3.18 mm |
>= 473 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 60.0 - 71.1 °C | 140 - 160 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3.00 hour | 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | USP Class VI | |
| Appearance | Natural Color | |
| Features | Biocompatible | |
| Good Chemical Resistance | ||
| Good Colorability | ||
| Medium Impact Resistance | ||
| Specialty Grade | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 33% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Hospital Goods | |
| Housings | ||
| Medical Appliances | ||
| Medical/Healthcare Applications |