PolyOne Syncure™ System S112NA Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer PolyOne Corporation
Trade Name Syncure™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Syncure™ System S112NA Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Syncure™ systems are two part moisture crosslinkable compounds. S112NA is a CSA listed, high strength, colorable power cable insulation compound and RoHS compliant.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.920 g/cc
0.920 g/cc
ASTM D792
Deformation 10 %

@Temperature 131 °C,
Time 3600 sec
10 %

@Temperature 268 °F,
Time 1.00 hour
500 g; UL 1581
Mechanical Properties Metric English Comments
Hardness, Shore D 47
47
10 sec; ASTM D2240
53
53
ASTM D2240
Tensile Strength, Yield 19.3 MPa
2800 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 400 %
400 %
Type IV, 510 mm/min; ASTM D638
Electrical Properties Metric English Comments
Dielectric Constant 2.24

@Frequency 1.00e+6 Hz
2.24

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 39.0 kV/mm
991 kV/in
ASTM D149
Dissipation Factor 0.00080

@Frequency 1.00e+6 Hz
0.00080

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Agency Ratings CSA C-22.2 0.3
IEC 60502
Appearance Natural Color
Catalyst Masterbatch 5%
S-1000B
Features Industrial Resin
Forms Pellets
Gel Content 72%
ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material XLPE
Generic Name Polyethylene, Crosslinked (XLPE)
Grafted Base Resin 95%
S-1054A
Processing Method Extrusion Coating
Regional Availability North America
Retention of Tensile Elongation 90%
121°C, 1.91 mm; 336 hr, UL Standard
Retention of Tensile Strength 95%
121°C, 1.91 mm; 336 hr, UL Standard
Uses Wire & Cable Applications
Wire Types NMD90
RW-90