PolyOne Stat-Tech™ PS-NX 102902 CM Black Polybutylene Terephthalate (PBT)  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Stat-Tech™ PS-NX 102902 CM Black Polybutylene Terephthalate (PBT)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data SheetPolyOne First ChoiceInformation provided by PolyOne Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Water Absorption 0.30 %
0.30 %
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0025 - 0.0040 cm/cm
0.0025 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 93.1 MPa
13500 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Elongation at Break 4.0 %
4.0 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 10.3 GPa
1500 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 172 MPa
25000 psi
ASTM D790
Flexural Modulus 10.3 GPa
1500 ksi
ASTM D790
Izod Impact, Notched 0.374 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
 0.700 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
 Method A, Injection Molded; ASTM D256
Electrical Properties Metric English Comments
Volume Resistivity 1000 - 1.00e+6 ohm-cm
1000 - 1.00e+6 ohm-cm
ASTM D257
Surface Resistivity per Square 1000 - 1.00e+6 ohm
1000 - 1.00e+6 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 243 - 277 °C
470 - 530 °F
Molding
Mold Temperature 82.2 - 110 °C
180 - 230 °F
Drying Temperature 82.2 - 110 °C
180 - 230 °F
Dry Time 2 hour
2 hour
Descriptive Properties Value Comments
Product Form Pellets