PolyOne Stat-Tech™ PI-05CF/000 EM Polyetherimide (PEI)  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Stat-Tech™ PI-05CF/000 EM Polyetherimide (PEI)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.Description/Features:PEI (Polyetherimide)5% Carbon Fiber ReinforcedESD ProtectionAntistaticStatic DissipativeApplications: EMI?RFI ShieldingPrinter ComponentsEnclosuresFuel SystemsProcessing Method: Injection MoldingInformation provided by PolyOne Corporation
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Water Absorption 0.25 %

@Thickness 3.17 mm
0.25 %

@Thickness 0.125 in
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 124 MPa
18000 psi
Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
Elongation at Break 4.0 - 5.0 %
4.0 - 5.0 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 4.48 GPa
650 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
Flexural Modulus 4.48 GPa
650 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
0.900 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 207 °C
405 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm - 1e+05
1000 ohm-cm - 1e+05
ASTM D257
Surface Resistivity per Square 1000 ohm - 1e+05
1000 ohm - 1e+05
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 354 - 382 °C
670 - 720 °F
Molding