PolyOne Stat-Tech™ NY-20CF/000 BLACK Polyamide 6 (Nylon 6)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ NY-20CF/000 BLACK Polyamide 6 (Nylon 6).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ASTM D792
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm	0.012 - 0.014 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	161 MPa	23400 psi	ASTM D638
Elongation at Break	2.4 %	2.4 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	12.1 GPa	1750 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	241 MPa	35000 psi	ASTM D790
Flexural Modulus	10.7 GPa	1550 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.899 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	219 °C @Thickness 6.35 mm	426 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	205 °C @Thickness 6.35 mm	401 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm - 1e+05	1000 ohm-cm - 1e+05	ASTM D257
Surface Resistance	1000 ohm - 1e+05	1000 ohm - 1e+05	ASTM D257
Static Decay	0.0020 sec	0.0020 sec	(Mil-B-81705C), 12% RH, 5000 kV to 50 kV

Processing Properties	Metric	English	Comments
Melt Temperature	238 - 277 °C	460 - 531 °F

Descriptive Properties	Value	Comments
Features	Good Chemical Resistance
	High Stiffness
	Semi Crystalline
Filler / Reinforcement	Carbon Fiber Reinforcement, 20% Filler by Weight
Forms	Pellets
Generic Material	Nylon 6
Generic Name	Polyamide 6 (Nylon 6)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Consumer Applications
	Electrical Housing
	Electrical/Electronic Applications
	Housings
	Sporting Goods