PolyOne Stat-Tech™ NN-20CF/000 Black Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Stat-Tech™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Stat-Tech™ NN-20CF/000 Black Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0050 cm/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
0.0010 - 0.0050 in/in

@Thickness 0.157 in,
Temperature 73.4 °F
Flow Bergmann Method; ISO 294-4
Linear Mold Shrinkage, Flow 0.00050 - 0.0020 cm/cm
0.00050 - 0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.017 - 0.019 cm/cm
0.017 - 0.019 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 172 MPa
24900 psi
ASTM D638
Elongation at Break 2.2 %
2.2 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 12.8 GPa
1860 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 231 MPa
33500 psi
ASTM D790
Flexural Modulus 11.9 GPa
1730 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
0.899 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 261 °C

@Thickness 6.35 mm
502 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C

@Thickness 6.35 mm
482 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 100 - 10000 ohm-cm
100 - 10000 ohm-cm
ASTM D257
Surface Resistance 100 - 10000 ohm
100 - 10000 ohm
ASTM D257
Static Decay 0.0030 sec
0.0030 sec
(Mil-B-81705C), 12% RH, 5000 kV to 50 kV
Processing Properties Metric English Comments
Melt Temperature 288 - 304 °C
550 - 579 °F
Descriptive Properties Value Comments
Features Good Chemical Resistance
High Stiffness
Semi Crystalline
Filler / Reinforcement Carbon Fiber Reinforcement, 20% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Aerospace Applications
Automotive Electronics
Business Equipment
Computer Components
Connectors
Consumer Applications
Electrical Housing
Electrical/Electronic Applications
Housings
Sporting Goods