PolyOne Stat-Tech™ MP-25NCF/000 Modified PPO - 25% Nickel Coated Graphite Fiber (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ MP-25NCF/000 Modified PPO - 25% Nickel Coated Graphite Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 6.35 mm |
1.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | <= 1.00 ohm-cm | <= 1.00 ohm-cm | ASTM D257 |
| Surface Resistance | <= 1.0 ohm | <= 1.0 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 293 - 316 °C | 559 - 601 °F | Stock |
| Mold Temperature | 82.0 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 93.0 °C | 199 °F |
Users viewing this material also viewed the following:
- RheTech Products FT3080-729UV Thermoplastic Polyolefin, UV Stabilized, AG-64 Grey
- Polymer Resources TP-IM1 Polybutylene Terephthalate, Low Temperature Impact Modified
- Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire
- Solvay TECHNYL® A 218G2 V30 Black 34N PA66, 30% glass fiber, Conditioned
- Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant
- ExxonMobil Mobil Delvac 15W-40 1300 Super
- Unifrax Fiberfrax® Fiberwall® 304 SS Systems Hardware
- Alliance Polymers Zythane™ 6070A Thermoplastic Polyurethane Elastomer
- Eurotec® Tecomid® NB40 NL RM PA 6 low friction and wear
Copyright © lookpolymers.com All Rights Reserved