PolyOne Stat-Tech™ AS-15CF/000 Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer PolyOne Corporation
Trade Name Stat-Tech™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Stat-Tech™ AS-15CF/000 Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Water Absorption 0.15 %

@Thickness 3.18 mm
0.15 %

@Thickness 0.125 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0015 - 0.0020 cm/cm
0.0015 - 0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 102 MPa
14800 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 2.5 - 4.0 %
2.5 - 4.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 3.96 GPa
574 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 141 MPa
20500 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
Izod Impact, Notched 0.760 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
1.42 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C

@Thickness 6.35 mm
185 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C

@Thickness 6.35 mm
167 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Flammability, UL94 HB
HB
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 100 - 50000 ohm-cm
100 - 50000 ohm-cm
ASTM D257
Surface Resistance 100 - 50000 ohm
100 - 50000 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 221 - 249 °C
430 - 480 °F
Mold Temperature 65.0 - 85.0 °C
149 - 185 °F
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 2.00 hour
2.00 hour
Descriptive Properties Value Comments
Features Electrically Conductive
Electromagnetic Shielding (EMI)
ESD Protection
Radio Frequency Shielding (RFI)
Filler / Reinforcement Carbon Fiber Reinforcement, 15% Filler by Weight
Forms Pellets
Generic Material ABS
Generic Name Acrylonitrile Butadiene Styrene (ABS)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Aerospace Applications
Automotive Under the Hood
Business Equipment
Electrical/Electronic Applications
Housings
Printer Parts