PolyOne Stat-Tech™ AS-08CF/000 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | PolyOne Corporation |
| Trade Name | Stat-Tech™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-08CF/000 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.25 % @Thickness 3.18 mm |
0.25 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.9 MPa | 9990 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 701 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 4.69 GPa | 680 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C @Thickness 6.35 mm |
210 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C @Thickness 6.35 mm |
205 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 - 1.00e+6 ohm-cm | 10000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 - 1.00e+7 ohm | 1e+05 - 1.00e+7 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 232 °C | 430 - 450 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Antistatic | |
| ESD Protection | ||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 8.0% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | ABS | |
| Generic Name | Acrylonitrile Butadiene Styrene (ABS) | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Aerospace Applications | |
| Automotive Under the Hood | ||
| Business Equipment | ||
| Electrical/Electronic Applications | ||
| Housings | ||
| Printer Parts |