PolyOne OnFlex™ HFFR 310-01 Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	OnFlex™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne OnFlex™ HFFR 310-01 Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OnFlex™ HFFR 310-01 is a non-halogen flame retardant material designed for cable jackets. New Product. Commercial specifications have not been established. - Non-halogen flame retardant - UL62 compliantPurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.01 g/cc	1.01 g/cc	ASTM D792
Viscosity	30000 cP @Shear Rate 11200 1/s, Temperature 200 °C	30000 cP @Shear Rate 11200 1/s, Temperature 392 °F	ASTM D3835
	1.10e+6 cP @Shear Rate 67.0 1/s, Temperature 200 °C	1.10e+6 cP @Shear Rate 67.0 1/s, Temperature 392 °F	ASTM D3835
Maximum Moisture Content	0.020	0.020
Deformation	15 % @Temperature 150 °C	15 % @Temperature 302 °F	2000g; UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	87	87	10 sec; ASTM D2240
Tensile Strength at Break	20.7 MPa	3000 psi	UL 1581
	15.2 MPa @Temperature 23.0 °C	2200 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
Elongation at Break	240 %	240 %	UL 1581
	230 % @Temperature 23.0 °C	230 % @Temperature 73.4 °F	Die C2 hr; ASTM D412
Tear Strength	42.8 kN/m	244 pli	ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	105 °C	221 °F	UL Temperature Rating; UL 1581
Brittleness Temperature	-40.0 °C	-40.0 °F	ASTM D746
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	BlackNatural; UL 94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	BlackNatural; UL 94
Oxygen Index	27 %	27 %	ASTM D2863-08

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.90e+15 ohm-cm @Temperature 23.0 °C	2.90e+15 ohm-cm @Temperature 73.4 °F	50% RH, ASTM D257-07; ASTM D257
Dielectric Strength	50.0 kV/mm @Thickness 0.533 mm, Temperature 23.0 °C	1270 kV/in @Thickness 0.0210 in, Temperature 73.4 °F	50% RH, ASTM D149-97a(04); ASTM D149

Processing Properties	Metric	English
Zone 1	180 - 190 °C	356 - 374 °F
Zone 2	200 - 210 °C	392 - 410 °F
Zone 3	210 - 220 °C	410 - 428 °F
Zone 4	210 - 220 °C	410 - 428 °F
Die Temperature	210 - 220 °C	410 - 428 °F
Drying Temperature	70.0 °C	158 °F
Dry Time	2.00 - 3.00 hour	2.00 - 3.00 hour

Descriptive Properties	Value	Comments
Agency Ratings	UL 94 .QMFZ2.E76261
Aging Resistance	100%	UL 1581; 136°C; Thermal aging tensile retention 168hrs.
	85%	UL 1581; 136°C; Thermal aging elongation retension168hrs.
Appearance	Black
	Natural Color
Features	Flame Retardant
Forms	Pellets
Generic Material	TPE
Generic Name	Thermoplastic Elastomer (TPE)
Manufacturer / Supplier	GLS Thermoplastic Elastomers
Processing Method	Extrusion
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Cable Jacketing
VW-1	pass	UL 1581