PolyOne Nymax™ NM 6600-44GF0001 White Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Nymax™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Nymax™ NM 6600-44GF0001 White Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Nymax® GMF 1200 Series of compounds are based upon nylon 6/6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part performance. These materials have been specifically formulated to offer ease of processing in most standard thermoplastic processing equipmentMolded Test Bars: Dry as MoldedInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 164 MPa
23800 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield 164 MPa
23800 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 2.4 %
2.4 %
Type I, 5.1 mm/min; ASTM D638
Flexural Yield Strength 286 MPa
41500 psi
13 mm/min; ASTM D790
Flexural Modulus 11.9 GPa
1730 ksi
13 mm/min; ASTM D790
Izod Impact, Notched 1.30 J/cm

@Thickness 3.18 mm
2.44 ft-lb/in

@Thickness 0.125 in
Injection Molded, 3.6 mm Notch Depth; ASTM D256A
Processing Properties Metric English Comments
Mold Temperature 48.9 - 93.3 °C
120 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance White
Filler / Reinforcement Glass Fiber Reinforcement, 44% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Processing Method Injection Molding
Regional Availability North America
Uses Construction Applications
Consumer Applications
Industrial Applications