PolyOne Nymax™ GF 604 35 HS Black 13 Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GF 604 35 HS Black 13 Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing enhanced surface appearance versus nylon 6/6 compounds. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipment.Molded Test Bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Strength, Yield | 152 MPa | 22000 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C @Thickness 3.18 mm |
394 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Appearance | Black | |
| Features | General Purpose | |
| Heat Stabilized | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 35% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | North America | |
| South America | ||
| Uses | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |