PolyOne Nanoblend™ LST 5571 Polypropylene, Unspecified (PP, Unspecified)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nanoblend™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nanoblend™ LST 5571 Polypropylene, Unspecified (PP, Unspecified).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nanoblend compounds, formerly known as Maxxam LST, are LIGHT, STIFF AND TOUGH. Using nanoclay technology, these compounds deliver a combination of high stiffness and impact resistance to meet demanding structural and durability requirements. At the same time, they offer the light weight, aesthetic and processing advantages that are more typical of polyolefins.Provisional Product Information - Physical and Mechanical properties based on initial production.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.948 g/cc | 0.948 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | Internal Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | 15 sec; ASTM D2240 |
| 72 | 72 | ASTM D2240 | |
| Tensile Strength, Yield | 30.3 MPa | 4390 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 19 % | 19 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 43.2 MPa | 6270 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 3.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
6.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.18 mm |
187 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.18 mm |
126 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Clay Nano Filler | |
| Forms | Pellets | |
| Generic Material | PP, Unspecified | |
| Generic Name | Polypropylene, Unspecified (PP, Unspecified) | |
| Regional Availability | North America | |
| South America |