PolyOne Maxxam™ SY 89-23-7 Polypropylene, Unspecified (PP, Unspecified)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Maxxam™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Maxxam™ SY 89-23-7 Polypropylene, Unspecified (PP, Unspecified).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Maxxam ™ SY 89-23-7 is a polypropylene copolymer compound with a pre-dispersed blowing agent for up to 60% expansion. The compound offers consistent cell structure, dielectric properties, and strength on insulation walls as thin as 10 mils.NOTE: 1. Typical properties of molded slab (0.075); Not to be construedas specifications.2. Foam density reduction depends upon loading level, temperatureand residence time before cooling.3. Recommended process temperature: 190°C to 220°C (375°F to430°F).Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.449 g/cc | 0.449 g/cc | ASTM D792 |
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.4 MPa | 3390 psi | Type IV, 510 mm/min; ASTM D638 |
| Elongation at Break | 400 % | 400 % | Type IV, 510 mm/min; ASTM D638 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.24 @Frequency 1000 Hz |
2.24 @Frequency 1000 Hz |
ASTM D150 |
| Dissipation Factor | 0.00030 @Frequency 1000 Hz |
0.00030 @Frequency 1000 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Foamable | |
| Forms | Pellets | |
| Generic Material | PP, Unspecified | |
| Generic Name | Polypropylene, Unspecified (PP, Unspecified) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Cable Jacketing | |
| Communication Wire Insulation | ||
| Wire & Cable Applications |